Geopolymer Fly Ash Building Brick by Atmospheric Curing

S. D. Muduli, B. D. Nayak and B. K. Mishra


In the current research work effort has been made to develop geopolymer fly ash building brick under atmospheric curing. Geopolymer building bricks are manufactured by using fly ash and alkaline soda based chemical activator solution in presence of sodium silicate and water by maintaining different Na2O/(Al2O3 + SiO2) ratio. During this work 230 × 110 × 75 mm size fly ash building bricks are manufactured under atmospheric curing. After 25 days of atmospheric curing the results shows that the geopolymer fly ash building bricks with Na2O/(Al2O3 + SiO2) ratio of 0.038 attain a crushing strength of 8.5 Mpa, which is approximately equal to the strength achieved by hot air curing at 90o C for 4 hrs.


अस्वीकृति: इस सारांश का अनुवाद कृत्रिम बुद्धिमत्ता उपकरणों का उपयोग करके किया गया है और इसे अभी तक समीक्षा या सत्यापित नहीं किया गया है।

में अनुक्रमित

  • कैस
  • गूगल ज्ञानी
  • जे गेट खोलो
  • चीन राष्ट्रीय ज्ञान अवसंरचना (सीएनकेआई)
  • उद्धरण कारक
  • ब्रह्मांड IF
  • इलेक्ट्रॉनिक जर्नल्स लाइब्रेरी
  • रिसर्च जर्नल इंडेक्सिंग की निर्देशिका (डीआरजेआई)
  • गुप्त खोज इंजन लैब्स
  • आईसीएमजेई

और देखें

जर्नल आईएसएसएन

जर्नल एच-इंडेक्स

Flyer

एक्सेस जर्नल खोलें