Giant magnetic anisotropy of Fe3Pt thin films at low temperature

M.A.I.Nahid, Takao Suzuki


The Fe3Pt alloy thin films were grown on MgO substrates at the various growth temperatures by e-beam evaporation in a high vacuum. The magnetic properties such as saturationmagnetization, coercivity,magnetic anisotropy etc. of the Fe3Pt alloy thin films were studied as a function of temperature varying in the range of 80Kto 600K.At lowtemperature (80K), the Fe3Pt films possessed giant cubic magnetic anisotropy (K1ï‚»7×106 erg/cc and K2ï‚»2.2×107 erg/cc). The magnetic anisotropy constants of Fe3Pt films were found to decrease slowly with temperature and vanished at Curie temperature. The Curie temperature of Fe3Pt thin films were also studied as a function of ordering. It was observed that higher ordered sample exhibited lower Curie temperature.


अस्वीकृति: इस सारांश का अनुवाद कृत्रिम बुद्धिमत्ता उपकरणों का उपयोग करके किया गया है और इसे अभी तक समीक्षा या सत्यापित नहीं किया गया है।

में अनुक्रमित

  • कैस
  • गूगल ज्ञानी
  • जे गेट खोलो
  • चीन राष्ट्रीय ज्ञान अवसंरचना (सीएनकेआई)
  • उद्धरण कारक
  • ब्रह्मांड IF
  • इलेक्ट्रॉनिक जर्नल्स लाइब्रेरी
  • रिसर्च जर्नल इंडेक्सिंग की निर्देशिका (डीआरजेआई)
  • गुप्त खोज इंजन लैब्स
  • आईसीएमजेई

और देखें

जर्नल आईएसएसएन

जर्नल एच-इंडेक्स

Flyer

एक्सेस जर्नल खोलें