Preparation and mechanism of nano-BaZrO3 by solid-state reaction at low temperature

Ding Shi-Wen, Zhang Yuan-Yuan, Zhang Hong-Jun


Nano-BaZrO3 was synthesized by Solid-State Reaction at Low temperature, useing Ba (OH) 2 • 8H2O and ZrOCl2 • 8H2O as raw materials. First, hydrolysis ZrOCl2 • 8H2O preparation of high-activity ZrO2 • H2O(H2ZrO3) then evenly grinding after mixtured with Ba (OH) 2 • 8H2O by 1:1 (mol), finallyDrying at 100 C reaction obtained a cubic bariumzirconic nanometer crystal. TEM photograph showed that they were uniform and substantially quadrate particles with the size of 40~80nm. The experiment Determined that the chemical reaction is rate controlling step at low temperature solid state reaction.


में अनुक्रमित

  • कैस
  • गूगल ज्ञानी
  • जे गेट खोलो
  • चीन राष्ट्रीय ज्ञान अवसंरचना (सीएनकेआई)
  • उद्धरण कारक
  • ब्रह्मांड IF
  • मियार
  • गुप्त खोज इंजन लैब्स
  • यूरो पब
  • यूनिवर्सिटैट डी बार्सिलोना
  • आईसीएमजेई

और देखें

जर्नल आईएसएसएन

जर्नल एच-इंडेक्स

Flyer

एक्सेस जर्नल खोलें