Susceptibility and curie temperature study in Cr3+ substituted Mg- Cd ferrites

S.A.Mastic


Temperature dependence normalized AC susceptibility and Curie temperature of spinel ferrites CdxMg1-xFe2-yCryO4 (x=0, 0.2, 0.4, 0.8 and 1.0; y=0, 0.05 and 0.1) study reveals that MgFe2O4 exibits multi domain (MD) structure with high Curie temperature On substitution of Cd2+,MDto Single Domain (SD) trasitions takes place and Curie temperature decreases due to decrease inA-B intraction. On substitution of Cr3+ inMg-Cd ferrite system peak obtained in MgFe2O4 is supressed which is attributed to decrease in grain size and further decrease in Curie temperature is attributed to the decrease in B-B interaction. This is because Fe-Fe interaction is greater than Cr-Fe interaction at B-site


अस्वीकृति: इस सारांश का अनुवाद कृत्रिम बुद्धिमत्ता उपकरणों का उपयोग करके किया गया है और इसे अभी तक समीक्षा या सत्यापित नहीं किया गया है।

में अनुक्रमित

  • कैस
  • गूगल ज्ञानी
  • जे गेट खोलो
  • चीन राष्ट्रीय ज्ञान अवसंरचना (सीएनकेआई)
  • उद्धरण कारक
  • ब्रह्मांड IF
  • रिसर्च जर्नल इंडेक्सिंग की निर्देशिका (डीआरजेआई)
  • गुप्त खोज इंजन लैब्स
  • आईसीएमजेई

और देखें

जर्नल आईएसएसएन

जर्नल एच-इंडेक्स

Flyer

एक्सेस जर्नल खोलें