ZnS nanocomposite nanorods prepared by simple method of chemical bath deposition

U.Baishya, D.Sarkar


ZnS nanocomposite nanorods have been prepared by chemical bath deposition technique taking Zinc acetate and Sodium sulphide as the source of Zinc and Sulphur respectively. The composite thin film is characterized by XRD, TEM, UV-Visible, PL and FTIR. Nanocrystalline thin film prepared under optimum growth condition shows band gap of 3.7eV as observed fromoptical absorption data. XRDshows peaks at 2 values of 28.50o, 47.58o and 56.39o for (111), (220), and (311) planes respectively.TEMmicrograph of the film reveals the formation of ZnS nanorods of diameter ranging from 15nmto 20nmand length from20nmto 220nm.Alongwith the rods there are some quasispherical small clusters also. Photoluminescence (PL) measurement showed blue emission centered at 413.5nmand green emission at 561nm.


अस्वीकृति: इस सारांश का अनुवाद कृत्रिम बुद्धिमत्ता उपकरणों का उपयोग करके किया गया है और इसे अभी तक समीक्षा या सत्यापित नहीं किया गया है।

में अनुक्रमित

  • कैस
  • गूगल ज्ञानी
  • जे गेट खोलो
  • चीन राष्ट्रीय ज्ञान अवसंरचना (सीएनकेआई)
  • उद्धरण कारक
  • ब्रह्मांड IF
  • इलेक्ट्रॉनिक जर्नल्स लाइब्रेरी
  • रिसर्च जर्नल इंडेक्सिंग की निर्देशिका (डीआरजेआई)
  • गुप्त खोज इंजन लैब्स
  • आईसीएमजेई

और देखें

जर्नल आईएसएसएन

जर्नल एच-इंडेक्स

Flyer

एक्सेस जर्नल खोलें